NTSB Cites 'A Chemically Milled Step' In Airplane Depressurization | Aero-News Network
Aero-News Network
RSS icon RSS feed
podcast icon MP3 podcast
Subscribe Aero-News e-mail Newsletter Subscribe

Airborne Unlimited -- Most Recent Daily Episodes

Episode Date

Airborne-Monday

Airborne-Tuesday

Airborne-Wednesday Airborne-Thursday

Airborne-Friday

Airborne On YouTube

Airborne-Unlimited-07.07.25

Airborne-NextGen-07.08.25

AirborneUnlimited-07.09.25

Airborne-FlightTraining-07.10.25

AirborneUnlimited-07.11.25

Sat, Aug 21, 2010

NTSB Cites 'A Chemically Milled Step' In Airplane Depressurization

"Preexisting Fatigue" Named As Probable Cause For A Hole Opening In A Southwest Airlines 737

The NTSB says "fuselage skin failure due to preexisting fatigue at a chemically milled step" is the probable cause for a 18x12 inch hole opening up in the roof of a Southwest Airlines 737 last year, causing the airplane to depressurize. No one was injured due to the incident.

NTSB Identification: DCA09FA065
Scheduled 14 CFR Part 121: Air Carrier operation of SOUTHWEST AIRLINES CO
Accident occurred Monday, July 13, 2009 in Charleston, WV
Probable Cause Approval Date: 8/18/2010 1:52:06 PM
Aircraft: BOEING 737, registration: N387SW
Injuries: 131 Uninjured.

Flight data recorder data revealed that the airplane took off and climbed for about 25 minutes to an altitude of approximately 35,000 feet, at which point the cabin altitude warning activated, and the captain disengaged the autopilot. Postincident examination of the airplane revealed fatigue cracking of the fuselage skin near the leading edge of the vertical stabilizer adjacent to the rupture. The fatigue cracking penetrated the fuselage skin and created an approximate 18-inch by 12-inch flap in the skin that depressurized the airplane.


NTSB Photo Exterior Skin

The fuselage skin assembly near the leading edge of the vertical stabilizer was manufactured by bonding two full aluminum sheets together, then selectively chemically milling away pockets (bays) of the inner sheet. Continuous fatigue cracks initiated from multiple origins on the inner surface of the skin adjacent to the step formed at the edge of the chemically milled area and propagated outward.

Following the Southwest Airlines (SWA) flight 2294 event, on September 3, 2009, Boeing issued Service Bulletin (SB) 737-53A1301, calling for repetitive external inspections to detect cracks in the fuselage skin along the chemically milled step at stringers S-1 and S-2 right and between BS 827 and BS 847. (The hole from the SWA event was within those boundaries.) If cracks are detected, operators are to contact Boeing for repair instructions. On January 12, 2010, the Federal Aviation Administration issued Airworthiness Directive 2010-01-09, which mandated the inspection requirements in SB 737-53A1301.


NTSB Photo Interior Skin

The airplane, serial number 26602, was delivered to SWA in June 1994. At the time of the SWA event, the airplane had accumulated approximately 42,500 cycles and 50,500 hours.

FMI: www.ntsb.gov

Advertisement

More News

NTSB Final Report: Aviat A1

Airplane Bounced About 3 Ft Then Touched Back Down And Then, With No Brakes Applied, The Airplane Began Veering To The Left Analysis: The pilot entered the airport traffic pattern >[...]

ANN's Daily Aero-Linx (07.08.25)

Aero Linx: British Microlight Aircraft Association (BMAA) The primary focus within all aviation activity is SAFETY. In all aspects of our sport SAFETY must come first, whether it b>[...]

Classic Aero-TV: Fly Corvair’s Reliable Engine Alternative

From SnF25 (YouTube Edition): William Wynne Builds Practical Aircraft Engines on the Corvair Platform Seeking an affordable alternative to the traditional aircraft engine options, >[...]

ANN FAQ: Contributing To Aero-TV

How To Get A Story On Aero-TV News/Feature Programming How do I submit a story idea or lead to Aero-TV? If you would like to submit a story idea or lead, please contact Jim Campbel>[...]

Classic Aero-TV: CiES Fuel-Quantity and e-Throttle Systems Praised

From 2023 (YouTube Edition): Bridge of CiES CiES Inc. is a Bend, Oregon-based designer and manufacturer of modular embedded aircraft systems and sensors. The company’s fuel-l>[...]

blog comments powered by Disqus



Advertisement

Advertisement

Podcasts

Advertisement

© 2007 - 2025 Web Development & Design by Pauli Systems, LC